Joint and Crack Sealing

Documents and materials:

 

Product name Product Description
MACSEAL 6690-4 MOD
Intended for cold weather applications in either asphalt or concrete pavements. Able to withstand up to 200% expansion at -29˚C. Excellent adhesion and cohesion properties while staying within the modified resiliency of 30-60%.
Lowest (tested) temperature without fracture: -38˚C (or lower)
MACSEAL 6690-1
Polymer modified cracksealant able to withstand moderate to low level expansion and contraction at -18 ˚C. Good adhesion and cohesion properties.
Lowest temperature without fracture: -31˚C
Oil Jacketed Kettle Material
MACSEAL 6690-1PM Polymer modified cracksealant designed with no crumb rubber content, able to withstand moderate expansion and contraction at -18˚ C. Good adhesion and cohesion properties.
Oil Jacketed Kettle Material
MACSEAL 6690-2
Polymer modified cracksealant designed to withstand colder more extreme expansion and contraction at -29˚C. For use in either asphalt or concrete pavements. Better adhesion and cohesion properties.
Lowest temperature without fracture: -34˚C
Oil Jacketed Kettle Material
MACSEAL 6690-4
Intended for applications that experience cold weather extremes colder than -29˚C.
Due to the nature of Low Modulus materials it is able to withstand up to 200% expansion while keeping excellent adhesion & cohesion properties intact.
Lowest (tested) temperature without fracture: -38˚C (or lower)
Oil Jacketed Kettle Material
MACSEAL DF Designed for applicators using Direct Fire Melters. MACSEAL DF is both adhesive and cohesive in nature and is usually used in moderate climates that experience cold weather of -18˚ C. Beram DF should be stirred or agitated while melting.
Direct Fire Kettles-Applicators

 

 

 

 

 

 

 

 

 

 

 

 

 

 

Description
MACSEAL 6690-4 MOD is a high performance, hot applied, single component extra low modulus joint and crack sealant. MACSEAL 6690-4 MOD is a very soft sealant that offers excellent low temperature bonding properties, while still maintaining a high degree of resiliency to reject incompressibles. MACSEAL 6690-4 MOD permits high elongation at cold temperatures with low stress development. MACSEAL 6690-4 MOD will not flow from the joint or be picked up by vehicle tires at high service temperatures.

Recommended Use
MACSEAL 6690-4 MOD is recommended for the large scale sealing of joints and random cracks in Portland cement concrete and asphaltic concrete pavements in cold climate areas.MACSEAL 6690-4 MOD was specifically formulated to provide extra protection against low temperature expansion and repeated freeze thaw cycles.

Coverage
MACSEAL 6690-4 MOD weighs approximately 9 lbs./gal (1.10 kg/L). A joint 7 mm deep by 50 mm wide, requires approximately 375 grams per 1 lineal meter.

Packaging
2 x 25 lb. polybags in a high strength corrugated cardboard container (50 lb/22.67 kg per box)
 

** For a detailed step by step application demonstration, please refer to this video.
 
 

 

Description
MACSEAL 6690-1 is a hot applied, single component joint and crack sealant. MACSEAL 6690-1 is a blend of asphalts, virgin polymers, synthetic rubbers and reinforcing fillers. MACSEAL 6690-1 offers advanced low temperature bonding properties, prolonged resistance to degradation from weather and a positive seal during the expansion and contraction of the joint or crack.

Recommended Use
MACSEAL 6690-1  is recommended for the large scale sealing of joints and random cracks in Portland cement concrete, and asphaltic concrete pavements.

Coverage
MACSEAL 6690-1  weighs approximately 9.6 lbs./gal (1.15 kg/L). A joint ½ x ½ “ (12.7 mm x 12.7 mm) requires approximately 12 lbs. per 100 lineal feet or 17.7 kgs per 100 lineal meters.

Packaging
• 450 lb. (205 kg), open top drums containing 10 individual 50 lb. pucks
• 2 x 25 lb. polybags in a high strength corrugated cardboard container
• 1 x 30 lb. polybags in a high strength corrugated cardboard container

** For a detailed step by step application demonstration, please refer to this video.
 

 

Description
MACSEAL 6690-1 PM is a hot applied, single component joint and crack sealant. MACSEAL 6690-1 PM is a blend of asphalts, virgin polymers and reinforcing fillers. MACSEAL 6690-1 PM offers advanced low temperature bonding properties, prolonged resistance to degradation from weather and a positive seal during the expansion and contraction of the joint or crack.
 
Recommended Use
MACSEAL 6690-1 PM is recommended for the large scale sealing of joints and random cracks in Portland cement concrete, and asphaltic concrete pavements.
 
Coverage
MACSEAL 6690-1 PM weighs approximately 9.6 lbs./gal (1.15 kg/L). A joint ½ x ½ “ (12.7 mm x 12.7 mm) requires approximately 12 lbs. per 100 lineal feet or 17.7 kgs per 100 lineal meters.
 

Packaging
• 450 lb. (205 kg), open top drums containing 10 individual 50 lb. pucks
• 2 x 25 lb. polybags in a high strength corrugated cardboard container
• 50 lb. steel pails

Joint and Crack Sealant Application Guidelines

** For a detailed step by step application demonstration, please refer to this video.
 

Description
MACSEAL 6690-2 is a premium quality, hot applied, single component joint and crack sealant. MACSEAL 6690-2 is a formulated blend of engineered asphalts, virgin polymers, synthetic rubbers, reinforcing fillers and anti-oxidant inhibitors. MACSEAL 6690-2’s unique blend offers excellent low temperature bonding properties, prolonged resistance to degradation from weather, and a positive seal during the expansion and contraction of the joint. MACSEAL 6690-2 remains ductile and highly resilient at low and high service temperatures.
 
Recommended Use
MACSEAL 6690-2 is recommended for the large scale sealing of joints and random cracks in Portland cement concrete and asphaltic concrete pavements.
 
Coverage
MACSEAL 6690-2 weighs approximately 9.6 lbs./gal (1.16 kg/L). A joint ½ x ½ “ (12.7 mm x 12.7 mm) requires approximately 12 lbs. per 100 lineal feet or 17.7 kgs per 100 lineal meters.
 

Packaging
• 450 lb. (205 kg), open top drums containing 10 individual 50 lb. pucks
• 2 x 25 lb. polybags in a high strength corrugated cardboard container
• 1 x 30 lb. polybags in a high strength corrugated cardboard container

 
** For a detailed step by step application demonstration, please refer to this video.
 

Description
MACSEAL 6690-4 is a high performance, hot applied, single component low modulus joint and crack sealant. MACSEAL 6690-4 is a very soft sealant that offers excellent low temperature bonding properties, while still maintaining a high degree of resiliency to reject incompressibles. MACSEAL 6690-4 permits high elongation at cold temperatures with low stress development. MACSEAL 6690-4 will not flow from the joint or be picked up by vehicle tires at high service temperatures.
 
Recommended Use
MACSEAL 6690-4 is recommended for the large scale sealing of joints and random cracks in Portland cement concrete and asphaltic concrete pavements in cold climate areas. MACSEAL 6690-4 was specifically formulated to provide extra protection against low temperature expansion and repeated freeze that cycles.
 
Coverage
MACSEAL 6690-4 weighs approximately 9 lbs./gal (1.10 kg/L). A joint ½ x ½ “ (12.7 mm x 12.7 mm) requires approximately 11 lbs. per 100 lineal feet or 16 kgs per 100 lineal meters.
 

Packaging
• 450 lb. (205 kg), open top drums containing 10 individual 50 lb. pucks
• 2 x 25 lb. polybags in a high strength corrugated cardboard container
• 50 lb. steel pails

 
** For a detailed step by step application demonstration, please refer to this video.
 

 

Description
MACSEAL DF (Direct Fire) is a single component joint and crack sealant specifically designed for use with Direct Fired, single walled melters. MACSEAL DF is manufactured using select engineered asphalt cements, polymers, select oil resins and UV inhibitors. MACSEAL DF will not flow from the joint or be picked up by vehicle tires, foot traffic, skateboards or roller blade wheels in high surface temperatures.
 
Recommended Use
MACSEAL DF was designed for the routine maintenance of asphalt concrete pavements or Portland Cement Concrete on driveways, parking lots, bicycle paths and walkways.
 
Coverage
Beram DF weighs approximately 9.5 lbs./gal (1.14 kg/L). A joint ½ X ½ (12.7 mm X 12.7 mm) requires approximately 12 lbs. Per 100 lineal feet or 17.7 kgs per 100 lineal meters
 
Packaging
• 2 x 25 lb. polybags in a high-strength corrugated cardboard container
• 1 X 30 lb. polybags in a high-strength corrugated cardboard container.
 
Copyright © 1995-2014 by Cantat Associates Inc. All Rights Reserved.